How to print matte dotting silicone effect on HD matte silicone printing?

How to print matte dotting silicone effect on HD matte silicone printing?

HD matte silicone ink printing process:

Preparation:

  1. Mesh&Squeegee: 120(48T) Mesh number; 65-75 degree Squeegee.
  2. : Pigments added ratio:For white and fluorescent color 20%,other color 10%
  3. Catalyst mixing ratio:2% 
  4. Silicone thinner XG-128AH adding ratio:0-20%    
  5. Heating Temp and time: Flash cure temp :100℃- 120for 6-10 seconds, Drying temp :120for about 2 –3 minutes.

1.Screen printing silicone print 3 layers:

Screen Printing silicone  XG-866A-2Y  100G

Silicone catalyst              XG-866B-2     2G   2%

Silicone thinner              XG-128AH   20G  20%

Flash temp 120 degree

If fabric with hairy or want to get more smooth effect kindly assist by heat press machine or iron after first time printing. After printing keeps wet to heat press by temp 150-170 degree for 10-20 seconds.

2.Black screen printing silicone print 5 layers

Screen Printing silicone  XG-866A-2Y  100G

Silicone catalyst              XG-866B-2     2G   2%

Black silicone pigment        XG-501     10G  10%

Silicone thinner              XG-128AH   20G  20%

Flash temp 120 degree

3.Matte screen printing silicone pri1 layer

Matte Printing silicone  XG-866M-6+  100G

Silicone catalyst              XG-866B-2     2G   2%

Flash temp 100 degree

4.Black silicone dotting print 5 layers

Screen Printing silicone  XG-866A-2Y  100G

Silicone catalyst              XG-866B-2     2G   2%

Black silicone pigment        XG-501     10G  10%

Silicone thinner              XG-128AH   20G  20%

Flash temp 120 degree

5.Matte silicone dotting print 1 layer:

Matte Printing silicone  XG-866M-6+  100G

Silicone catalyst              XG-866B-2     2G   2%

Flash temp 100 degree

After finish to dry by temp :120℃ for about 2 -3 minutes.

XG silicone HD matte dotting silicone printing

Share this post